RTV-2 electrical electronic silicone potting casting encapsulating adhesive glue sealant

INTRODUCTION

APS SC-1015 is two part, solvent free, silicone sealant cured in room temperature. It is one kind of high elasticity organosilicon pouring sealant for electronic components.

SPECIFICATION

Item

Qualification

Uncured

Appearance

A part: water clear, black, gray.

B part: water clear, black, gray.

Gravity(g/ml)

0.9±0.01

Viscosity(cP)

A part: 1800±50

B part: 10±1

Mix viscosity(cp)

1500±50

Operational time(h)

0.5~1.0

Initial curing time(h)

2~4

Completely curing time(h)

8

Cured

Strength of extension/MPa

≥1.2

Elongation at break /%

≥180

linear shrinkage /%

≤0.3

Dielectric strength(Kv/mm)

≥20

Volume resistivity /Ω.cm

≥1.0×1014

SHORE A

10±1

USAGE

Stir A, B parts well respectively, then mix A and B well according A:B=100:10.

Encapsulation after mixed well (suggest to the vacuum debubbling).

If the poured components are tinny and multiple-slot, continuous pouring to be advised.

If pouring depth is more than 6mm, curing time will be longer.

NOTICE

B part should be seal preservation.

Curing time can be adjusted by B part. More B part, higher curing speed.

Avoid closed environment and high ambient temperature more than 60°C when curing.

STORAGE

Storage: in a cool and dry place.

PACKING

22Kg/pcs(A part 20Kg+B part 2Kg)



This member's information has NOT been authenticated or verified by importexportleads.net or any third party. Only Gold Members have completed an authentication and verification procedure conducted by third-party credit agencies.

For more information on importexportleads Gold Membership, Click here

Contact Information

Company:
 Xiamen Aibeisen Electronic Co., Ltd.
Phone Number:
  86-592-3218029
Fax Number:
 86-592-5096568