Why choosing us:

One of top 3 building waterproof material manufacturer in China Professional and powerful R&D team to support technical service Four big factories are distributed in 4 big areas of China Get involved many big projects in China and Southeast Asia ,such as subway,tunnel,civil building,comercial building etc. Excellent exported experience,exported to America,Australia,Russia ,Europe,Malaysia,Dubai,Middle east etc ISO quality and environment friendly certificate

E-929 Single-component Polyurethane Waterproof Coating

E-929 can be applied on wet surface and complicated projects with its unique mechanism of reaction by atmospheric moisture and the NCO end group of the PUP to form a seamless, strong bonding, elastic and flexible waterproof film.

Product features

One-component packaging, ready to use, avoid unstable condition when mixingAnti-aging, acid & alkali resistance, high & low temperature resistance performanceEnvironment friendly: conform to the harmful substances standard GB 50325-2001Apply combine with high polymer membrane, self-adhesive polymer modified-bitumen waterproof membrane.High bonding strength, high adhesion, excellent performance

Applicable scope

Non-exposed roof, underground projects, kitchen & bath and non-drinking water project

Application procedures

Preparation →Substrate treatment → Detail parts treatment → Apply the bottom layer as treatment → Scrape the coating → acceptance → Cover the protective layer

main points of application

♦The surface should be clean and firm, repair flaw part beforehand.

♦Detail parts treatment: Coat a layer on the internal and external corners and the part of pipeline bottom, and then apply reinforce layer (non-alkali fiberglass fabric or non-woven fabric), make sure that the coating saturate completely the reinforce layer.

♦Application of basement layer: you may add some basic primer to strength the closure and permeability.

♦Multi-layer application: apply the coating on the substrate evenly, and then apply with vertical direction for next coating. The surface drying time is about 12 hours, the waiting time base on the first layer which touch to be non-stick, generally apply 2~3 times (or according to the design requirements).

♦The thickness of the coating should be 0.5~0.8mm.

♦Recommended application for substrate: primer: principal material = 1:2 (weight), apply after mixing.

Performance index

No.	Item		I	II
1	tensile strength (Mpa) ≥		1.9	2.45
2	elongation at break % ≥		550	450
3	tear strength (N/mm) N/mm ≥		12	14
4	foldability at low temperature °C≤		-40
5	impermeability( 0.3Mpa, 30min)		impermeable
6	solids content %≥		80
7	surface drying time, h≤		12
8	hard drying time, h≤		24
9	heat shrinkage %	≤	1.0
		≥	-4.0
10	cohesive strength of moist base surface, Mpa ≥		0.50
11	outspread aging	heat aging	no gash or deformation
		artificial weathering aging	no gash or deformation
12	heat treatment	retention rate of tensile strength %	80-150
		elongation at break % ≥	500		400
		foldability at low temperature °C	-35
13	alkali treatment	retention rate of tensile strength %	60-150
		elongation at break % ≥	500		400
		foldability at low temperature °C	-35
14	acid treatment	retention rate of tensile strength %	80-150
		elongation at break % ≥	500		400
		foldability at low temperature °C	-35
15	artificial weathering aging	retention rate of tensile strength %	80-150
		elongation at break % ≥	500		400
		foldability at low temperature °C	-35